Electrochemically-induced TiO2 incorporation for enhancing corrosion and tribocorrosion resistance of PEO coating on 7075 Al alloy
2018
Abstract 7075 Al alloy was PEO-treated in a silicate based electrolyte containing 3 g l-1 potassium titanyl oxalate using unipolar and bipolar pulsed current waveforms. The coating formed by the bipolar waveform with the wider cathodic pulses showed volcano-like surface morphology with no evidence of large pores at the metal/coating interface. It revealed the highest corrosion performance due to the synergistic effect of TiO2 incorporation and structural/morphological features along with a better passivation behavior indicating no pitting susceptibility. For this coating, the tribocorrosion tests showed no potential drop during sliding under 1 N with the lowest volume loss of 0.022 mm3.
Optical polarization of nuclear ensembles in diamond
2012
We report polarization of a dense nuclear-spin ensemble in diamond and its dependence on magnetic field and temperature. The polarization method is based on the transfer of electron spin polarization of negatively charged nitrogen vacancy color centers to the nuclear spins via the excited-state level anti-crossing of the center. We polarize 90% of the 14N nuclear spins within the NV centers, and 70% of the proximal 13C nuclear spins with hyperfine interaction strength of 13-14 MHz. Magnetic-field dependence of the polarization reveals sharp decrease in polarization at specific field values corresponding to cross-relaxation with substitutional nitrogen centers, while temperature dependence o…